Hot Work Die Steel Round Bar (H13/SKD61/1.2344)

- Sep 14, 2017-

Basic Info

  • Model NO.: 1.2344, H13, SKD61, 4Cr5MoSiV1

  • Standard: AISI, ASTM, DIN, JIS, GB, BS

  • Technique: Hot Rolled

  • Surface Treatment: Black, Black/Polish/Machined

  • Application: Die Steel Bar

  • Ut Class: According to Standard of Sep 1921/84, 100% Volume

  • Process Technique: Hot Forged or Rolled

  • Trademark: kaixin

  • Specification: diameter 12-160mm

  • HS Code: 7228300000

  • Type: Round

  • Composition: Mould Steel

  • Shape: Round

  • Special Use: Wear Resistant Steel

  • Model Number: DIN 1.2343 /SKD61 Hot-Work Die Steel

  • Melting Process: Eaf+ESR

  • Payment Term: L/C at Sight or T/T

  • Transport Package: Export Standard Packing or Customers′demand

  • Origin: China

Product Description

H13 Steel Plates Alloy Tool Steel
Die-casting mould for aluminum, extrusion mould, and thin-wall plastics mould.

1, SKD61 Features
A, Good heat-resistance and fatigue-resistance.
B, Good cutting and polishing performance.
C, May be cold-hobbed in the annealed condition.
D, Very good red-hardness with toughnes.

2, SKD61 Application
A, Suitable to manufacturing aluminum, zinc, copper alloy extrusion die, die casting, 

hot forging die and hot shear blades, etc.
B, Extrusion mold of aluminum and magnesium, die-casting mold, 

especially adapt to the mold in large and complicated form.
C, Used for making hot squeeaing mould,forging mould and embedded lump.

3, SKD61 Heat Treatment:
The first stage of preheating:500 ~ 550 oC
The second stage of preheating:750 ~ 800 oC
Cooling or high pressure gas cooling, 100 ~ 150 oC in the tempering furnace.
Preheat:300 ~ 350 oC
Tempering heating:550 ~ 680 oC
Air cooling to room temperature, tempering three times.

Quenching temperature 1000 ~ 1050 degrees, 50 to 55 HRC hardness, 

heat treatment deformation is small, can be nitriding surface nitriding processing, 

processing of products has better wear resistance.

4, SKD61 Hardness:Annealing 235 ~ 205 HB, quenching ≥50 HRC

5, Delivery Detail:For abundant stock, 15-20 days.

For customized products, 30-50 days.

6, Grade


7, Chemical composition(%)



Delivery condition:

EAF or ESR, Hot rolled or Forged, machined material, Hardness:HBS=160-235.

Ultrasonic test standards:

SEP1921-84 GR.3 CLASS D/D

Picture shows