DIN 1.2379 Cold Mould Steel for Industry

DIN 1.2379 Cold Mould Steel for Industry


Product Details

Introduction:

D2 is a high carbon - high chromium air hardening tool steel, heat treatable to 60-62 Rc. D2 offers excellent wear and abrasion resistance, due to large volumes of carbides in the microstructure. D2 is widely used in long production cold work applications requiring very high wear resistance and high compression strength. It is machinable in the annealed condition, and, like other air hardening tool steels, exhibits minimal distortion in heat treat. D2 is available in de-carb free rounds, flats, and squares, as well as ground flat stock and drill rod.

 

Chemical Composition:

Steel Grade

C

Si

Mn

Cr

Mo

V

  P

S

D2

1.40-1.60

0.10-0.60

0.10-0.60

11.00-13.00

0.7-1.0

0.15-0.30

≤0.03

≤0.03

 


 Applications include:

Typical applications for D2 tool steel are blanking, forming, and trim dies, gages, slitting cutters, wear parts, lamination dies, thread rolling dies, drawing dies, rotary cutting dies, knurls, bending dies, gages, shear blades, burnishing tools, rolls, machine parts, master parts, injection screw and tip components, seaming rolls, extrusion dies, tire shredders, scrap choppers, etc.

 

Forging:

Heating for forging must be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often as necessary, stopping work when the temperature drops below 1700°F. After forging, cool slowly in lime, mica, dry ashes or furnace. D2 should always be annealed after forging.

 

Annealing:

Heat slowly to 1550°-1600°F, hold until entire mass is heated through, and cool slowly in the furnace (40°F per hour) to about 1000°F, after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.

 

Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168

FAX0714-6519746

Emailinfo@hubeikaixin.com

AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei

Code435000

web:www.kxdiesteel.com 


Inquiry