Tool Die Steel 5CrNiMo

Tool Die Steel 5CrNiMo

Chat Now

Product Details

Tool die steel 5CrNiMo

Quick Details

Steel Grade: tool die steel SKT4

Standard: AISI, ASTM, BS, DIN, GB, JIS

Dimensions: optional

Place of Origin: Hubei, China (Mainland)

Brand Name: KAIXIN

Technique: Hot Rolled

Application: Die Steel Bar

Alloy Or Not: Is Alloy

Special Use: Mold Steel

Type: Alloy Steel Bar

Standared: AISI ASTM BS DIN GB JIS

dIemsions:30mm-400mm

features: free cutting, polishing performance

special use: production of large, medium-sized ,aluminum die-casting mold

Packaging & Delivery

Packaging Details standared seaworthy packing

Specifications

6 years experience 
throughISO9001/2000 
first hand the pre-sale price 
on-time delivery 
variety of payment options

Specifications

 

1. Foged Alloy Steel Round Bar 
2.excellent cutting and polishing performance 
3.large, medium-sized aluminum die-casting mold 

 

1. Forged Alloy Steel Round Bar

2.Good high temperature strength, toughness and resistance to high temperature performance and can withstand sudden changes in temperature, suitable for long-term work at high temperatures, with excellent free cutting and polishing performance, quenching temperature of 1020 °C. Is the best material for production of large, medium-sized aluminum die-casting mold

3.Special Use

This steel is easy to turning, and are advised to sharp knife, scissors, circular saw, cold or hot for molding, Rollers, screw, milling-tool,.......and so on

4.Advantages

(1) vacuum degassing refining, internal quality is extremely clean

(2) good machinability

(3)Excellent hardenability don't worrying about the quenching crack

(4) heat treatment distortion is very small, the quenching deviation is minimal, the most suitable for there accuracy requirements of the mold

(5) Excellent wear resistance, used for stainless steel or hard materials

(6)good toughness

5.Chemical composition(for reference only):

C

Si

Mn

Mo

V

Cr

P

S


1.50

0.25

0.45

1.00

0.35

12.00

≤0.025

≤0.01


6.Heat treatment Quenching: preheat to 700 ~ 750 °C, and then heated to 1000 ~ 1050 ° C in still air cooling, such as steel with a thickness of 6 inches or more heating to 980 ~ 1030 ° C in oil hardened better. Tempering: heating to 150 ~ 200 °C, stay at this temperature and then cooling in still air. Hardness: HRC 61 or more. Annealing: heating to 800 ~ 850 °C, at this temperature for 1 to 3 hours, let it getting cold.

Forged: 1050 ~ 950 °C.

blob.png 

Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168

FAX0714-6519746

Emailinfo@hubeikaixin.com

AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei

Code435000

web:www.kxdiesteel.com 

 


Inquiry